POLYETHYLENE
Density: 0,92- 0.96 kg/cm3
Tensile Strength: 15-30 MPa
Flexural Modulus: 1000-1500MPa
Impact Strength: 4-10 kj/m²
Deformation Temp.: 100-110 ºC
Vicat Softening Temp.: 120-130 ºC
POLYPROPYLENE
Specific Gravity : 0,91 gr/cm³
Tensile Strenght : 30-40 MPa
Flexural Modulus : 1400-1600 MPa
IZOD Impact Strenght : 5-10 kj/m²
Heat Deflection Temperature : 110 ºC
Vicat Softening Temperature: 150 ºC
POLYPHENYLENE OXIDE
Density: 1.29g/cm3
Tensile Strength: 120 MPa
Flexural Modulus: 10.000 MPa
Izod Impact Strength: 9-10 KJ/m2
Deformation Temp. : 120 ºC
POLYSTRENE
Specific Gravity :1.04 g/cm³
Tensile Strenght :40-50 MPa
Flexural Modulus :2100-2200 MPa
IZOD Impact Strenght :140-150 kj/m²
Heat Deflection Temperature :93 ºC
Vicat Softening Temperature :100 ºC
POLYACETYLENE
Specific Gravity : 1.41
Tensile Strenght : 95 MPa
Flexural Modulus : 2500-2600 MPa
IZOD Impact Strenght : 55-60 kj/m²
Heat Deflection Temperature : 110 ºC
Vicat Softening Temperature : 162 ºC
POLYCARBONATE
Specific Gravity : 1.20
Tensile Strenght : 63-70 MPa
Flexural Modulus : 2400-2500 MPa
IZOD Impact Strenght : 80-85 kj/m²
Heat Deflection Temperature: 130 ºC
Vicat Softening Temperature :150 ºC